KINGROON PA Nylon Carbon Fiber 3D Printer Filament
Secure Payment Methods
All transactions are secure and encrypted
KINGROON PA Nylon Carbon Fiber 3D Printer Filament
Why Choose Our PLA Filament
Our PLA filament is engineered to deliver stable, repeatable results across a wide range of 3D printers.Whether you're printing functional parts or detailed models, it helps reduce failed prints and wasted material.
No More PLA Printing Headaches
ired of clogged nozzles, tangled spools, warped edges, or prints that fail halfway through?
This PLA filament is designed to deliver smooth extrusion, stable feeding, and reliable layer bonding across everyday print jobs.
Spend less time troubleshooting and more time finishing prints you can trust.
Before/after image slider
Before
After
Consistent Flow
Delivers consistent diameter for clog-free printing
Low Warp
Low warping and easy to use for beginners
Eco Friendly
Eco-friendly material made from renewable resources
Wide Fit
Wide compatibility with most FDM 3D printers
Eco-friendly
Kingroon PLA filament is made from plant-based starches like corn and cassava. This renewable, plant-based material is biodegradable and eco-friendly, posing no harm to the environment.
High Accuracy and Quality
Dimensional accuracy of +/- 0.03mm. Rigorous quality control ensures consistent filament dimensions, keeping your 3D printing tangle-free.
Neat Winding
Neat winding minimizes the filament tangle, ensuring a smooth printing experience.
Vibrant Color Selection
Choose from our extensive palette of vibrant, consistent colors that maintain their appearance after printing.
Recently Viewed Products
3D printing material properties
Fully understand the printing settings, physical properties, and mechanical performance of the materials to optimize your 3D printing experience.
| Nozzle Temp（℃） | 190-210 |
|---|---|
| Bed Temp（℃） | 50-70 |
| Fan | 100% |
| Length | (1.75mm) 330-340m |
| Density | 1.23g/cm³ |
|---|---|
| Melt Index | 12-15(190℃/216kg)g/10min |
| Distortion Temp | 53℃(0.45MPa) |
| Izod impact strength | 3.9 kj/m² |
| Tensile strength | ≥ 38 MPa |
|---|---|
| Elongation at break | 0.15 |
| Bending strength | 60MPa |
| Flexural modulus | 2700MPa |
| Nozzle Temp（℃） | 190-210 |
|---|---|
| Bed Temp（℃） | 50-70 |
| Fan | 100% |
| Length | (1.75mm) 330-340m |
| Density | 1.23g/cm³ |
|---|---|
| Melt Index | 12-15(190℃/216kg)g/10min |
| Distortion Temp | 53℃(0.45MPa) |
| Izod impact strength | 3.9 kj/m² |
| Tensile strength | ≥ 38 MPa |
|---|---|
| Elongation at break | 0.15 |
| Bending strength | 60MPa |
| Flexural modulus | 2700MPa |
Printing Tips
Dry Before Use
Dry before use to ensure the best print quality and consistent finish. Drying conditions: In a blast drying oven: 50°C for 8 hours; In an AMS 2 Pro and AMS HT: 55°C, 8 hours; On an X1 printer's heatbed: 60°C to 70°C for 12 hours. Store in a dry environment after use.
Filament drying instructions on WIKI →Using Refill Filament